CAS No.: | 123-45-5 |
---|---|
Formula: | C8h4o3.C4h10o3.C4H2O3 |
Molecular Principal Chain: | Carbon Chain Polymer |
Color: | White |
Viscosity: | 0.15-0.25 PA.S |
Type: | Synthetic Resin and Plastics |
Suppliers with verified business licenses
orthophthalic unsaturated polyester resin synthesized from improved Phthalic anhydride and standard diols. Has been dissolved in styrene monomer, with moderate viscosity and reactivity.
Product name :Liquid raw material polyester casting resin | |
Product Model : 6674A | |
Demishion : 220kg/barrel | |
Usage : Casting high property solid surface materials countertop bathtub bathroom accessories | |
Feature 1 : Light color and high transparent | |
Feature 2 : Low sharkage and fast curing | |
Feature 3 : Excellent hardness and weather resistance |
Property Index of polyester resin
Appearance | Acid value | Solid content | Viscosity25ºC | Gel time |
- | mgKOH/g | % | pa.s | min |
Light yellow viscous liquid | 14-20 | 64-70 | 0.55-0.90 | 4.5-10.0 |
Casting Properties of polyester resin
Appearance | Pasteurian hardness | Tensile Strength | Tensile modulus of elasticity | elongation at break | bending strength | Bending elastic modulus | Impact strength | Heat distortion temperature |
- | shore | MPa | MPa | % | MPa | MPa | KJ/m2 | ºC |
Casting with no blemish | 40 | 60 | 3100 | 3.5 | 110 | 3200 | 12 | 60 |
Notes: Polyester resin includes wax but no accelerator and thixotropic agent
Colorless Accelerator mixed ratio :0.8%-1.5% of polyetser resin
Hardener mixed ratio : 1.5%-2.0% of polyester resin
Application
This Liquid raw material polyester resin has low hue and high transparency fast curing high strength as well as good climate resistance ,fit for casting high property bathroom accessories and Solid surface material as well Translucent stone.
Item
|
Range
|
unit
|
Testing method
|
appearance
|
Light yellow viscous liquid
|
-
|
GB/T 8237.4.1.1
|
Acid value
|
25-30
|
mgKOH/g
|
GB/T 2895
|
Viscosity,25ºC
|
0.25-0.45
|
Pa.s
|
GB/T 7193.1
|
Solid content
|
61-70
|
%
|
GB/T 7193.3
|
Gel time ,25ºC
|
9-17
|
min
|
GB/T 7193-2008
|
Item
|
Unit
|
Measured value
|
Testing method
|
Barco hardness
|
--
|
41
|
GB 3854-83
|
Heat distortion temperature
|
ºC
|
70
|
GB 1634-04
|
Bending strength
|
MPa
|
112
|
GB/T 2570-95
|
Tensile Strength
|
MPa
|
60
|
GB/T 2568-95
|
Elongation at break
|
%
|
3.5
|
GB/T 2568-95
|
Impact strength
|
KJ/m2
|
10.2
|
GB/T 2571-95
|
Item
|
Unit
|
Measured data
|
Testing method
|
Bending strength
|
MPa
|
365
|
GB/T1449-83
|
Tensile Strength
|
MPa
|
290
|
GB/T1447-83
|