Plastic Properties After Heated: | Thermoplastic Plastics |
---|---|
Plastic Forming Method: | Injection |
Ratio: | 120-200% |
Scrappage: | Low |
Glossiness: | Glossy |
Application: | Widely Used to Produce Slippers, Shoes |
Samples: |
---|
Suppliers with verified business licenses
PROPERTIES
|
TEST METHOD
|
UNIT
|
VALUE
|
Melt Flow Index(230ºCx2.16kg)
|
ASTM D-1238
|
g/10 min
|
2.5
|
Density
|
ASTM D-792
|
g/cm3
|
0.938
|
Vinyl Acetate content
|
-
|
%
|
18
|
Tensile Strength at Yield
|
ASTM D-638
|
kg/cm2
|
45
|
Tensile Strength at break
|
ASTM D-638
|
kg/cm2
|
150
|
Tensile Elongation at break
|
ASTM D-638
|
%
|
800
|
Rockwell hardness
|
ASTM D-785
|
R scale
|
100
|
Soften point
|
ASTM D-1525
|
ºC
|
60
|
Melting point
|
DSC
|
ºC
|
84
|
Brittleness point
|
ASTM D746
|
ºC
|
<-70
|
Advantage:
1. Our goods have excellent quality and competitive price.
2.Our comapny export of EVA materials for more than 18 years.
Content of VA
|
Application range
|
<5%
|
Film, wire and cable, LDPE modifier, adhesive, etc
|
5%~10%
|
Elastic film, injection molding and foaming products, etc
|
20% ~ 28%
|
Mainly used for hot melt adhesives and coating products
|
28% - 33%.
|
Photovoltaic materials, solar cell adhesives, etc
|
38% - 40%
|
Adhesive
|
Packing