Plastic Properties After Heated: | Thermoplastic Plastics |
---|---|
Plastic Forming Method: | Injection |
Ratio: | 120-200% |
Scrappage: | Low |
Glossiness: | Glossy |
Application: | Widely Used to Produce Slippers, Shoes |
Samples: |
---|
Suppliers with verified business licenses
EVA16%
|
|||
PROPERTIES
|
TEST METHOD
|
UNIT
|
Data
|
VA Content
|
|
%
|
16
|
Density
|
ASTM D1505
|
g/cm3
|
0.937
|
Melt Index MI2.16
|
ASTM D1238
|
g/10min
|
1.5
|
Tensile Strength (Break)
|
ASTM D638
|
Kg/cm2
|
170
|
Elongation at break
|
ASTM D638
|
%
|
700
|
Melting point
|
ASTM D-3418
|
ºC
|
89
|
Hardness
|
ASTM D2240
|
Shore D
|
37
|
EVA 18%
|
|
||
Properties
|
Test method
|
Value
|
|
VA Content(%)
|
USI
|
18
|
|
Density(g/cm3)
|
ASTM D792
|
0.939
|
|
Melt Index (g/10min)
|
ASTM D1238
|
2.5
|
|
Tensile Strength(Molded)(Break)(kg/cm2)
|
ASTM D638
|
180
|
|
Ultimate elongation(Molded)(%)
|
ASTM D638
|
750
|
|
Low Temperature Brittleness(ºC/F50)
|
ASTM D746
|
<-76
|
|
Vicat Softening Point(ºC)
|
ASTM D1525
|
64
|
|
Melt Point (ºC)
|
ASTM D3418
|
86
|
|
Hardness(Shore D)
|
ASTM D2240
|
36
|
|
EVA28%
|
|
||
PROPERTIES
|
TEST METHOD
|
UNIT
|
Data
|
VA Content
|
|
%
|
28
|
Density
|
ASTM D1505
|
g/cm3
|
0.954
|
Melt Index MI2.16
|
ASTM D1238
|
g/10min
|
15
|
Tensile Strength (Break)
|
ASTM D638
|
Kg/cm2
|
80
|
Elongation at break
|
ASTM D638
|
%
|
>800
|
Melting point
|
ASTM D-3418
|
ºC
|
69
|
Hardness
|
ASTM D2240
|
Shore D
|
20
|
Advantage:
1. Our goods have excellent quality and competitive price.
2.Our comapny export of EVA materials for more than 18 years.
Content of VA
|
Application range
|
<5%
|
Film, wire and cable, LDPE modifier, adhesive, etc
|
5%~10%
|
Elastic film, injection molding and foaming products, etc
|
20% ~ 28%
|
Mainly used for hot melt adhesives and coating products
|
28% - 33%.
|
Photovoltaic materials, solar cell adhesives, etc
|
38% - 40%
|
Adhesive
|
Suppliers with verified business licenses